Title: | Alumina-Based Composites Reinforced with Ductile Particles | Keywords: | Fracture toughness;Ductile particles;Reinforcement;Alumina;Composites;info:eu-repo/classification/cti/2 | Publisher: | International Journal of Research in Engineering and Science (IJRES) | Project: | Vol.;2 No.;6 |
Description: | Al2O3/Metal composite ceramics were fabricated by the use of mechanical milling and pressureless sintering. Al2O3 + 10 vol.% of La, Mn, Si or Y were mixed and milled during 12 h at 300 rpm in a horizontal mill, then with the powder mixture it was conformed cylindrical samples by uniaxial pressing using 300 MPa. Pressed samples were sintered during 2 h in an electrical furnace at 1500°C. During sintered it was used an argon atmosphere inside the furnace in order to inhibit metal oxidation. XRD results indicate that alumina and metals retain its crystalline structure. Reached density by samples is small and less than 90%. Scanning electron microscopy observations show alumina’s microstructure with very fine and homogeneous distributions of metal particles. Both the Mn and Si are not suitable metals to improve the mechanical properties of alumina, in particular the fracture toughness. Considered rare earth metals such as yttrium and lanthanum, have yielded favorable results in improving the fracture toughness of the alumina. However, it should be made more dense materials with them to better explore this potential. | URI: | http://ri.uaemex.mx/handle20.500.11799/65165 | Other Identifiers: | http://hdl.handle.net/20.500.11799/65165 | Rights: | info:eu-repo/semantics/openAccess http://creativecommons.org/licenses/by-nc-nd/4.0 |
Appears in Collections: | Producción |
Show full item record
Google ScholarTM
Check
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.