Thickness effect on electric resistivity on polystyrene and carbon black- based composites

Abstract

Changes on electrical resistivity were experimentally studied for polystyrene and carbon black-based composites respect to the temperature. 22% w/w carbon black composite films at 30 μm, 2mm y 1cm thick were submitted to thermal heating-cooling cycles from room temperature to 100°C, slightly up to Tg of the composite. For each cycle changes on electrical resistivity constituent a hysteresis loop that depends on the sample thickness. The changes during the heating stage could be explained as a consequence of the thermal expansion and mobility of the polymer chains at Tg, producing a disconnecting of the electrical contacts among carbon black particles and an important increasing (200%) of the electrical resistivity. For each cycle, the hysteresis loop was observed in thicker samples, whereas for 30 ? m thickness sample the hysteresis loop was lost after four cycles.